AKROMID® A3 GF 30 S1 natural (3695)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iOuyTo_AKROMID-A3-GF-30-S1-natural-3695-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 30 S1 natural (3695) is a 30% glass fibre reinforced, low-temperature impact resistant Polyamid 6.6 with high stiffness and strength. Applications are precisions parts in automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.34 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 60.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.30 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.7 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 8000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 180 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 280 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 110 | -- | kJ/m² | |
| 23°C | 110 | 97 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 253 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene Lotrène® Q2018 H | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| Nylfor® A2 GB/30 FR2/3A UV BLACK | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Nylene® NX4747 | Custom Resins Group | Nylon Copolymer | Nylene® |
| Polifor® 5020/V2 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| Sylvin 9812-65 White 1514 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |