Osterlene® HIPS0802

Category:	PS (HIPS) , High Impact Polystyrene
Manufacturer:	Osterman & Company
Trademark:	Osterlene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	iOtKTv_OsterleneHIPS0802.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

HIPS0802 is a high impact polystyrene for injection molding.

The polymer's ability to be molded on fast cycles with minimal stresses results in outstanding impact retention.

Applications such as appliance housings, housewares, toys and structural foam require This polymer to produce consistent parts.

General Information
Features	Impact resistance, high
Uses	Electrical appliances Household goods Toys
Agency Ratings	FDA 21 CFR 177.1640
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	8.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2280	MPa	ASTM D638
Tensile Strength (Yield)	24.8	MPa	ASTM D638
Tensile Elongation (Break)	50	%	ASTM D638
Flexural Modulus	2340	MPa	ASTM D790
Flexural Strength	46.2	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	110	J/m	ASTM D256
Instrumented Dart Impact	14.1	J	ASTM D3029

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Annealed)	91.1	°C	ASTM D648
Vicat Softening Temperature	96.1	°C	ASTM D1525

Optical	Nominal Value		Test Method
Gardner Gloss (60°)	88		ASTM D523

Resin Grade	Manufacturer	Category	Trademark
Sylvin 5208-78 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
KRATON® G2705 GU-N	Kraton Polymers LLC	SEBS	KRATON®
Karina WHITE PVC COMPOUND -E 835-10/156-C-ERYB	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
POCAN® B 3225 XF 000000	LANXESS GmbH	PBT	POCAN®
LNP™ LUBRICOMP™ KFL36 compound	SABIC Innovative Plastics	Acetal (POM) Copolymer	LNP™ LUBRICOMP™