Minlon® EFE6053 BK413
| Category: | Nylon 66 , MINERAL REINFORCED NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Minlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iOgEV3_Minlon-EFE6053-BK413.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Mineral/Glass Reinforced Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 5.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.5 | -- | % | |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 160 | 97.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | 4.6 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 6000 | MPa | |
| 1000 hr | -- | 3700 | MPa | |
| Flexural Modulus | 9900 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 6.0 | kJ/m² | |
| 23°C | 4.5 | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 40 | kJ/m² | |
| 23°C | 45 | 50 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 256 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 70.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.8E-5 | -- | cm/cm/°C | |
| Transverse | 8.7E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength | 28 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.90 | 13.9 | ||
| 1 MHz | 4.80 | 5.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.014 | 0.54 | ||
| 1 MHz | 0.013 | 0.070 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.25 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 1900 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.27 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY66-IM2-(color)H | Polymer Resources Ltd. | Nylon 66 | PRL |
| Sylvin 8215-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ABSCOM® SE180 | Polymer Compounders Limited | ABS | ABSCOM® |
| Clariant Nylon 6 PA-212 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| DAI-EL™ G-763F | Daikin Fluorochemicals (China) Co., Ltd. | Fluorelastomer | DAI-EL™ |