TECACOMP® PA6 CF30 black 3553
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iO5S6H_TECACOMPPA6CF30black3553.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | |
| Apparent Density | 0.58 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.72 | % | ISO 294-4 |
| Flow | 0.14 | % | ISO 294-4 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18000 | MPa | ISO 527-2/50 |
| Tensile Stress | 230 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 213 | °C | ISO 75-2/A |
| Glass Transition Temperature | DIN 53765 | ||
| -- 1 | 5.00 | °C | DIN 53765 |
| -- 2 | 60.0 | °C | DIN 53765 |
| Melting Temperature | 220 | °C | DIN 53765 |
| Service Temperature | |||
| long term | 100 | °C | |
| short term | 180 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electrical Conductivity | 130 | S/m | ISO 3915 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 0.72 | ohms·cm | ISO 3915 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 250 - 300 | °C | |
| Mold Temperature | 80 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | Moist |
| 2 . | Dry |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3862 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Prixene® PC350I00C | POLYMAT | PP Copolymer | Prixene® |
| TARODUR 100 G3 | Taro Plast S.p.A. | ABS | TARODUR |
| 3M™ Dyneon™ PTFE Compound TF 7149 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Paxon™ AB50-003 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |