Hylac® EX19 Datasheet,ABS,Entec Polymers-SHANGHAI SUSHENG

Message
Hylac®EX19 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America and is processed by blow molding or extrusion. Hylac®The main features of EX19 are: ROHS certification Impact resistance

General Information
Features	Ultra-high impact resistance
RoHS Compliance	RoHS compliance
Forms	Particle
Processing Method	Blow molding Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.03	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)
230°C/3.8 kg	0.30	g/10 min	ASTM D1238
220°C/10.0 kg	3.3	g/10 min	ISO 1133
Molding Shrinkage - Flow	0.30 - 0.70	%	ASTM D955

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	90		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2140	MPa	ASTM D638
Tensile Strength (Yield, 23°C)	31.0	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	46	%	ASTM D638
Flexural Modulus (23°C)	2070	MPa	ASTM D790
Flexural Strength (Yield, 23°C)	59.3	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
23°C, 3.18 mm	480	J/m	ASTM D256
23°C, 6.35 mm	370	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	92.2	°C	ASTM D648
1.8 MPa, not annealed	82.2	°C	ASTM D648
Vicat Softening Temperature	104	°C	ASTM D1525

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+15	ohms·cm	ASTM D257

Additional Information
Volume Resistivity, ASTM D257: >10^15

Extrusion	Nominal Value	Unit
Drying Temperature	85.0	°C
Drying Time	3.0	hr
Suggested Max Moisture	0.020	%
Cylinder Zone 1 Temp.	191 - 210	°C
Cylinder Zone 2 Temp.	191 - 210	°C
Cylinder Zone 3 Temp.	199 - 221	°C
Cylinder Zone 4 Temp.	199 - 221	°C
Cylinder Zone 5 Temp.	199 - 221	°C
Adapter Temperature	221 - 241	°C
Die Temperature	221 - 241	°C

Extrusion instructions
Hylac ABS extrusion grade resins should be dried to a moisture content of 0.02% or less prior to processing. Control of the outer stock temperature is important in successfully finishing the product. Typical temperatures of outer stock range from 160°F to 175°F after passing through a water bath. The bath temperature profile will greatly affect the dimensional stability and appearance of the part, and if not set up properly could be detrimental to the ultimate mechanical strength of the product. Extruders with one-stage or two-stage force venting are recommended for the extrusion of sheets or profiles. Compression ratios should be between 2.5/1 and 3.0/1 for a single screw and between 1.5/1 and .0/1 for a two-stage screw. L/D ratios of 20/1 and 36/1 are typical.Process Parameter:Zone 6: 430-465°FZone 7: 430-465°FOuter Die Zone: 435-475°FMid Die Zone: 430-465°FCenter Die Zone: 420-465°FDie Lip Thickness: 3.2-4.0 mmNip Roll Top: 185-195°FNip Roll Middle: 175-185°FNip Roll Bottom: 165-175°FScreen Pack Mesh (2 layers): #60-80Extrusion parameters were found by extruding 3.2mm thick sheets at a haul off speed of 1368 mm/min and an output rate of 210 kg/hr. A polishing roll in a up stack wrap arrangement was used as well as a single screw with a 100mm diameter screw, a L/D ratio of 35/1, and a compression ratio of 3/1.

Extrusion instructions

Hylac ABS extrusion grade resins should be dried to a moisture content of 0.02% or less prior to processing. Control of the outer stock temperature is important in successfully finishing the product. Typical temperatures of outer stock range from 160°F to 175°F after passing through a water bath. The bath temperature profile will greatly affect the dimensional stability and appearance of the part, and if not set up properly could be detrimental to the ultimate mechanical strength of the product. Extruders with one-stage or two-stage force venting are recommended for the extrusion of sheets or profiles. Compression ratios should be between 2.5/1 and 3.0/1 for a single screw and between 1.5/1 and .0/1 for a two-stage screw. L/D ratios of 20/1 and 36/1 are typical.Process Parameter:Zone 6: 430-465°FZone 7: 430-465°FOuter Die Zone: 435-475°FMid Die Zone: 430-465°FCenter Die Zone: 420-465°FDie Lip Thickness: 3.2-4.0 mmNip Roll Top: 185-195°FNip Roll Middle: 175-185°FNip Roll Bottom: 165-175°FScreen Pack Mesh (2 layers): #60-80Extrusion parameters were found by extruding 3.2mm thick sheets at a haul off speed of 1368 mm/min and an output rate of 210 kg/hr. A polishing roll in a up stack wrap arrangement was used as well as a single screw with a 100mm diameter screw, a L/D ratio of 35/1, and a compression ratio of 3/1.

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	Entec Polymers
Trademark:	Hylac®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	iLUXtP_Hylac-EX19.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 800 TFE 20 LP	RTP Company	Acetal (POM) Copolymer	RTP
Greene 965	Greene, Tweed & Co.	NBR	Greene
LNP™ STAT-KON™ DEL22P compound	SABIC Innovative Plastics	PC	LNP™ STAT-KON™
Polifil® Nylon 628L-33GF	The Plastics Group	Nylon 66	Polifil® Nylon
LEXAN™ EXL1890T resin	SABIC Innovative Plastics	PC	LEXAN™