DOW™ LLDPE DNDB-7147 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iIqzkA_DOW-LLDPE-DNDB-7147-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Preparation of DNDB-7147 NT 7 Linear Low Density Polyethylene (LLDPE) Resin Using UNIPOL™PE process technology for injection molding such as food containers, household appliances and cover materials. This resin has an excellent balance between impact strength, rigidity, environmental stress cracking resistance and processability. Main features:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.926 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 50 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 5.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 9.65 | MPa | ASTM D638 |
| Fracture | 7.58 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | ASTM D638 |
| Fracture | 120 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 421 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 189 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 45.0 | °C | ASTM D648 |
| Brittleness Temperature | -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 109 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® 520350M | ELASTO | SEBS | Mediprene® |
| AEI SX523:CM493 and SX523:CM497 | AEI Compounds Limited | LDPE | AEI |
| AKROMID® B3 GF 50 S1 natural (3694) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Cheng Yu FR3410-NH | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| HONES® PPS HS-CT15-G | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |