Desmovit® DP R 9918

Category:	TPU-Ester/Ether , Thermoplastic Polyurethane Elastomer (Ester/Ether)
Manufacturer:	geba Kunststoffcompounds GmbH
Trademark:	Desmovit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	iIV82B_Desmovit-DP-R-9918.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Ether-based injection molding type with a ratio of 20% glass fiber

Characteristics:

very high stiffness, extreme impact strength and flexibility at low temperature, very good hydrolysis and microbial resistance, seawater proof, good UV resistance, high shock resistance & high fl exibility, good noise absorption, excellent colorability and printability

Applications:

mechanically highly stressed components of technical applications (indoor and outdoor), protectors for skiing, horse riding and motor sports, fishing net sinker, helmets, winter sport products such as ski tips, ski edge protection parts, ski bindings, ski boots, goggles, housings in the offshore area

General Information
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Features	Excellent Printability Good Colorability Good Flexibility Good UV Resistance High Impact Resistance High Stiffness Hydrolysis Resistant Low Temperature Flexibility Microbe Resistant Salt Water/Spray Resistant Shock Resistant Sound Damping
Uses	Outdoor Applications Safety Equipment Safety Guards Safety Helmets Sporting Goods
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.29	g/cm³	ISO 1183/A
Molding Shrinkage
Across Flow	0.32	%
Flow	0.10	%

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	64		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	59.0	MPa	ISO 527-2/200
Tensile Strain (Break)	17	%	ISO 527-2/200
Flexural Modulus ¹			ISO 178
-30°C	3000	MPa
23°C	1800	MPa
Flexural Stress ²			ISO 178
-30°C	118	MPa
23°C	54.0	MPa
Abrasion	80	mm³	ISO 4649

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	22	kJ/m²
23°C	45	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break
23°C	No Break

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	167	°C	ISO 75-2/B
1.8 MPa, Unannealed	126	°C	ISO 75-2/A
Vicat Softening Temperature	92.0	°C	ISO 306/B50
CLTE			DIN 53752
Flow	1.0E-5	cm/cm/°C
Transverse	1.1E-4	cm/cm/°C

Injection	Nominal Value	Unit
Drying Time	2.0	hr
Processing (Melt) Temp	200 to 230	°C
Mold Temperature	40.0 to 80.0	°C

Note Message
1 .	1.0 mm/min
2 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
POLYMAN® (ABS) E/HI	A. Schulman Europe	ABS	POLYMAN®
RheTech Thermoplastic Polyolefin FT6140-01UV	RheTech, Inc.	Polyolefin, Unspecified	RheTech Thermoplastic Polyolefin
Veroplas K18	PlastxWorld Inc.	Acrylic (PMMA)	Veroplas
UBE Polyethylene F023	UBE America, Inc.	PE, Unspecified	UBE Polyethylene
Gallonprene® GP210-4511	Shenzhen Sungallon Rubber & Plastic Corporation Limited	TPE	Gallonprene®