Panlite® LN-2525ZA
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iHdgWk_Panlite-LN-2525ZA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame resistant grade, Weather resistant grade |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.50 to 0.70 | % | |
| Flow : 4.00 mm | 0.50 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 62.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Flexural Stress 2 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 141 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 129 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 148 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 7.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C | |
| RTI Elec (1.50 mm) | 125 | °C | UL 746 |
| RTI Imp (1.50 mm) | 115 | °C | UL 746 |
| RTI Str (1.50 mm) | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.10 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 825 | °C | |
| 3.00 mm | 875 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Light Transmission (3.00 mm) | Translucent | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultralloy™ 910-5C | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Kepamid® 1333GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| Latamid 66 H2PX-V2 | LATI S.p.A. | Nylon 66 | Latamid |
| Ultramid® A3HG6 HR | BASF Corporation | Nylon 66 | Ultramid® |
| Moplen EP300H | LyondellBasell Industries | PP Impact Copolymer | Moplen |