VAMPLUB C 00U 4TF
| Category: | PC , Polycarbonate |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPLUB |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iHLHpF_VAMPLUB-C-00U-4TF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC unfilled with PTFE. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.70 | % | |
| Across Flow | 0.70 | % | |
| Water Absorption (Saturation) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Coefficient of Friction | ASTM D1894 | ||
| Dynamic | 0.14 | ||
| Static | 0.18 | ||
| Wear Factor 1 | 70.0 | 10^-10 m³ h/N·m·h |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 100 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648A |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 |
| Note Message | |
|---|---|
| 1 . | Thrust Washer |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2405 MAS056 | Covestro - Polycarbonates | PC | Makrolon® |
| RTP 205 L | RTP Company | Nylon 66 | RTP |
| DILAMID® 66 FVT 35 NAT A | Dilaplast S.p.A. | Nylon 66 | DILAMID® |
| Hostalen CRP 100 RESIST S blue | LyondellBasell Industries | HDPE | Hostalen |
| KYOCERA KE-G3000DA | KYOCERA Chemical Corporation | Epoxy | KYOCERA |