CoolPoly® D5506
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iHDtnV_CoolPoly-D5506.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly D series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The D series is electrically non-conductive and can be used for its dielectric properties. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.80 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 | % | |
| Across Flow | 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10900 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 0.70 | % | ISO 527-2 |
| Flexural Modulus | 12300 | MPa | ISO 178 |
| Flexural Stress | 84.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.2 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | > 300 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 263 | °C | ISO 75-2/A |
| CLTE | ASTM E831 | ||
| Flow | 6.2E-6 | cm/cm/°C | |
| Transverse | 5.6E-6 | cm/cm/°C | |
| Specific Heat | 1000 | J/kg/°C | ASTM E1461 |
| Thermal Conductivity | 10 | W/m/K | ASTM E1461 |
| Thermal Diffusivity | 5.00 | cSt | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| High Voltage Arc Resistance to Ignition (HVAR) | > 5.0 | min | UL 746 |
| Surface Resistivity | 2.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.6E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 46 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 4.50 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 0.020 | ||
| 1 MHz | 2.0E-3 | ||
| Arc Resistance | 300 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | V | ASTM D3638 |
| Hot-wire Ignition (HWI) | > 120 | sec | ASTM D3874 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 180 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Dew Point | -34.0 | °C | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 330 to 360 | °C | |
| Middle Temperature | 340 to 370 | °C | |
| Front Temperature | 345 to 380 | °C | |
| Nozzle Temperature | 350 to 382 | °C | |
| Processing (Melt) Temp | 349 to 393 | °C | |
| Mold Temperature | 93.0 to 177 | °C | |
| Injection Pressure | 34.4 to 70.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 6.89 to 34.5 | MPa | |
| Back Pressure | 0.00 to 0.350 | MPa | |
| Screw Speed | 75 to 150 | rpm | |
| Cushion | 10.0 to 13.0 | mm | |
| Screw Compression Ratio | 3.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ A70 GK30 H NC132 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| DOMAMID® 66G20 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Eltex® Superstress™ CAP602 | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| LEXAN™ LGK4010 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina IVORY PVC COMPOUND 70900-35/1 1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |