Trademark PE LLB1918C

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Trademark Plastics Corporation
Trademark:	Trademark PE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	iH4oT8_Trademark-PE-LLB1918C.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Trademark PE LLB1918C is a linear low density polyethylene product,. It is available in North America. The application fields of Trademark PE LLB1918C include bag/lining, packaging, film and food contact applications.

Features include:

Antiblock software

Butene Comonomer

accessible food

Good sealing performance

Puncture resistance

General Information
Additive	High caking resistance
Features	Butene comonomer High caking resistance Perforation resistance Good stripping Good heat sealability Compliance of Food Exposure
Uses	Packaging Films Lining Food packaging Heavy packing bag
Agency Ratings	FDA 21 CFR 177.1520(c) 3.1a
Forms	Particles

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
secant modulus			ASTM D882
1% secant, MD : 25 µm, blown film	186	MPa	ASTM D882
1% secant, TD : 25 µm, blown film	190	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Broken, 25 µm, blown film	45.5	MPa	ASTM D882
TD : Broken, 25 µm, blown film	31.7	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Broken, 25 µm, blown film	570	%	ASTM D882
TD : Broken, 25 µm, blown film	730	%	ASTM D882
Dart Drop Impact (25 µm, Blown Film)	110	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, blown film	130	g	ASTM D1922
TD : 25 µm, blown film	320	g	ASTM D1922

Optical	Nominal Value		Test Method
Gloss (45°, 25.4 µm, Blown Film)	45		ASTM D2457

Extrusion	Nominal Value	Unit
Melt Temperature	204 - 232	°C

Extrusion instructions
Blow-up ratio: 1.5:1 or higher

Resin Grade	Manufacturer	Category	Trademark
RTP 203D GB 10 TFE 13 SI 2	RTP Company	Nylon 612	RTP
RTP 307 SE	RTP Company	PC	RTP
Axiall PVC 19853	Axiall Corporation	PVC, Flexible	Axiall PVC
Jackdaw PP EV13BN6469	Jackdaw Polymers	PP, Unspecified	Jackdaw PP
KMI PP KM-616IB	KMI Group, Inc.	PP Impact Copolymer	KMI PP