ARC ARC2301
| Category: | PC , Polycarbonate |
| Manufacturer: | ARC Resin Corporation |
| Trademark: | ARC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iGK5Dh_ARC-ARC2301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ARC ARC2301 is a Polycarbonate (PC) material. It is available in North America. Primary attribute of ARC ARC2301: Flame Rated. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.18 mm) | 58.6 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.18 mm) | 130 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.18 mm) | 2340 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.18 mm) | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 750 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 129 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm, All) | V-2 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T-27 GF 15 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Trexprene® A70CI-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| ExTima™ GP MB LCP 530 | Ovation Polymers Inc. | LCP | ExTima™ |
| HiFill FR® ABS GF10 FR | Techmer Engineered Solutions | ABS | HiFill FR® |
| Karina BLACK PVC COMPOUND 751D48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |