FRIANYL® A3 V0XI
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | FRIANYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iGB75Y_FRIANYL-A3-V0XI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRIANYL® A3 V0XI is an unfilled Polyamide 66 (Nylon 66) compound, 25% flame retardant with halogens, free from antimony trioxide, PBB and PBDE, UL listed V0. This compound is intended for injection molding. FRIANYL® A3 V0XI is primarily designed for the Electrical and Electronic industry. It is also suitable for Automotive or Industrial & Consumer applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.0 | % | |
| Flow : 23°C | 1.0 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.0 | % | |
| Saturation, 23°C | 6.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 56.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 2.5 | % | |
| Break, 23°C | 4.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ISO 75-2/A |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (3.20 mm, Solution A) | 350 | V | IEC 60112 |
| Needle Flame Test | IEC 60695-11-5 | ||
| 1.00 mm | Pass | ||
| 2.00 mm | Pass |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | |
| 3.20 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 800 | °C | |
| 3.20 mm | 775 | °C | |
| Oxygen Index | 34 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC6-1080U | Spartech Polycom | ASA | Spartech |
| TEREZ SAN 2012 G | TER HELL PLASTIC GMBH | SAN | TEREZ SAN |
| Fainplast PVC PH 50/AL | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Elvax® 450 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Hostacom PF062-2 NA NATURAL | LyondellBasell Industries | PP Homopolymer | Hostacom |