Nypol® PA A3 G30 P20 PRTA010 NR428 MSP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iFr8af_Nypol-PA-A3-G30-P20-PRTA010-NR428-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in color black lead reinforced with 30% of fiberglass and PTFE 20% blended , good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.3 | % | ASTM D570 |
| Ash Content | 28 to 32 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ASTM D638 |
| Tensile Strength | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 9700 | MPa | ASTM D790 |
| Flexural Strength | 190 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 245 | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 285 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 905 | RTP Company | PSU | RTP |
| NYCOA Polyamide 2011 | Nycoa (Nylon Corporation of America) | Nylon+TPE | NYCOA Polyamide |
| Infino WP-1041 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| Karina IVORY PVC COMPOUND 105900-35/1 1-B-ACE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Piolen® P G10CA35 | PiO Kunststoffe GmbH & Co KG | PP Copolymer | Piolen® P |