LNP™ STAT-KON™ WS002I compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iFAOt0_LNP-STAT-KON-WS002I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON WS002I is a compound based on PBT resin containing 10% Stainless Steel. Added features of this material include: Electrically Conductive, High Impact. Also known as: LNP* STAT-KON* Compound WS-HI Product reorder name: WS002I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.30 | g/cm³ | ASTM D792 |
| -- | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2270 | MPa | ASTM D638 |
| -- | 2150 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/5 |
| Break 3 | 35.0 | MPa | ASTM D638 |
| Break | 34.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 4.2 | % | ISO 527-2/5 |
| Break 5 | 16 | % | ASTM D638 |
| Break | 17 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2030 | MPa | ASTM D790 |
| -- 7 | 1920 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 67.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 63.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D256 |
| 23°C 9 | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 10 | 70 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.20 | J | ASTM D3763 |
| -- | 7.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 173 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 115 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 59.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 58.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 4.0 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7727 | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Zhongfa PA66 ST-06 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 66 | Zhongfa |
| CALIBRE™ 301 HMR FC030003 | Trinseo | PC | CALIBRE™ |
| Sylvin 8773-60D Brown 7361 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| Sylvin 9812-65 Brown 7418 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |