LNP™ THERMOCOMP™ PF003 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iEaGIS_LNP-THERMOCOMP-PF003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* PF003 is a compound based on Nylon 6 resin containing 15% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PF-1003 Product reorder name: PF003 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6360 | MPa | ASTM D638 |
| Tensile Strength (Break) | 123 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.2 | % | ASTM D638 |
| Flexural Modulus | 5610 | MPa | ASTM D790 |
| Flexural Strength | 179 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 203 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® TE30CW | BASF Leuna GmbH | Nylon 66/6 | Miramid® |
| VENYL UFC200 | AD majoris | Nylon 66 | VENYL |
| Delta PPR-2G40 | Delta Polymers | PP Copolymer | Delta |
| ISPLEN® PB 180 A4M | REPSOL | PP Impact Copolymer | ISPLEN® |
| OP - PC - Filled/Lubricated 15 PTFE-30GF | Oxford Polymers | PC | OP - PC - Filled/Lubricated |