NYCOA Polyamide 567
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iD0eWl_NYCOA-Polyamide-567.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 567 is a general-purpose unextracted Nylon 6 resin, which offers superior flexibility and toughness in both molding and extrusion applications. It has a moderately high melt viscosity, excellent processability, and yields extremely tough and resilie NYCOA 567 resin has acceptance in diversified fields from grass cutting-line, to extruded soft-hand fishing line, and other monofilament applications. It is available with custom additive packages: heat stabilizer, UV stabilizer, flame retardant and/or cu NYCOA 567 can be certified to MIL-M-22096, Type IVA Nylon. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 2.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 66.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 3 | 965 | MPa | ASTM D790 |
| Flexural Strength 4 | 46.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 215 | °C | DSC |
| Additional Information |
|---|
| Relative Viscosity, NYCOA Method: 2.9 to 3.2 SAVWater Extractable, NYCOA Method: 8 to 10 %Tensile Elongation at Break, ASTM D638, 2in/min: 300+%The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G25 202 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Trexprene® A74BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| ACCUTECH™ HP0336M40CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| GETILAN GPE/400 M | Crosspolimeri S.p.A. | XLPE | GETILAN |
| Hifax TYC 900P C11301 | LyondellBasell Industries | PP, Unspecified | Hifax |