Comco PA 66 GF 30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Comco-Plastic GmbH |
| Trademark: | Comco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iCqgmI_Comco-PA-66-GF-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Comco PA 66 GF 30 is a Polyamide 66 (Nylon 66) material filled with 30% glass fiber. It is available in Europe. Primary attribute of Comco PA 66 GF 30: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ||||
| Saturation, 23°C | 5.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | |
| Water Absorption | ISO 62 | |||
| after 24 h immersion in water : 23°C | 30.0 | -- | mg | |
| after 96 h immersion in water : 23°C | 56.0 | -- | mg |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Maximum Service Temperature | ||||
| in air continuosly | 120 | -- | °C | |
| in air for short periods | 240 | -- | °C | |
| Service Temperature - Minimum | -20 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 76 | -- | ISO 2039-2 | |
| Ball Indentation Hardness | 165 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 5900 | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 100 | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 5.0 | 12 | % | ISO 527-2 |
| Tensile Creep Modulus 1(1000 hr) | 26.0 | 18.0 | MPa | ISO 899-1 |
| Compressive Stress | ISO 604 | |||
| 5% Strain | 90.0 | -- | MPa | |
| 2% Strain | 55.0 | -- | MPa | |
| 1% Strain | 28.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | > 50 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 6.0 | 11 | kJ/m² | ISO 180/2A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | -- | °C | ISO 75-2/A |
| Melting Temperature | 255 | -- | °C | |
| CLTE - Flow | ||||
| 23 to 60°C | 5.0E-5 | -- | cm/cm/°C | |
| 23 to 100°C | 6.0E-5 | -- | cm/cm/°C | |
| Thermal Conductivity | 0.30 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | > 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.90 | 6.90 | ||
| 1 MHz | 3.60 | 3.90 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.012 | 0.19 | ||
| 1 MHz | 0.014 | 0.040 | ||
| Comparative Tracking Index | 475 | 475 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 3.00 mm | HB | -- | ||
| 6.00 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | 1% Strain |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® H 649 FH | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| Axiall PVC 9113J Clear 13 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Generic ASA+Nylon | Generic | ASA+Nylon | Generic |
| Lustran® ABS 750 | Styrolution | ABS | Lustran® ABS |
| KIBISAN® PN-106 L150 FG | CHI MEI CORPORATION | SAN | KIBISAN® |