| Unreinforced Polyamide 612 |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ||||
| Flow : 3.20 mm | 1.1 | -- | % | Internal Method |
| Across Flow : 3.20 mm | 1.1 | -- | % | Internal Method |
| Across Flow | 1.4 | -- | % | ISO 294-4 |
| Flow | 1.3 | -- | % | ISO 294-4 |
| Water Absorption | ||||
| 24 hr | 0.40 | -- | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 3.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.3 | -- | % | ISO 62 |
| Viscosity Number | 95.0 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 62.0 | 54.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.5 | 18 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 17 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2100 | 1440 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | 3.0 | kJ/m² | |
| 23°C | 3.5 | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | 40 kJ/m² | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 4.5 | 3.0 | kJ/m² | |
| 23°C | 4.0 | 4.5 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 135 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 65.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 181 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 218 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.1E-4 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 9.0E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.6E-4 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 9.0E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.8E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.850 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 0.900 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2750 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.18 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-HM-FR2-(color)-3 | Polymer Resources Ltd. | PC | PRL |
| Ghaed ABS ABS-GH-500 | Ghaed Basir Petrochemicals Co. | ABS | Ghaed ABS |
| Huafon JF-S-M8090 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina CLEAR PVC COMPOUND 45/203-DA-ATB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexar® PX1164 | LyondellBasell Industries | EVA | Plexar® |