Andur 80-5 AP/Curene® 442
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iAdCbz_Andur-80-5-AP-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 80-5AP is a polyether (PTMG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 83-85 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 80-5AP with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 0.676 | MPa | ASTM D695 |
| 10% strain | 1.68 | MPa | ASTM D695 |
| 15% strain | 2.87 | MPa | ASTM D695 |
| 25% strain | 4.38 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.38 | MPa | ASTM D412 |
| 300% strain | 9.69 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 36.5 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 580 | % | ASTM D412 |
| Compression Set | 28 | % | ASTM D395B |
| Bayshore Resilience | 55 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 6.0 - 7.0 | min | |
| Demold Time | 30 | min | |
| Post Cure Time (96°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 81 to 85Die C Tear, ASTM D1004: 425 pliAverage Split Tear, ASTM D1938: 130 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 80-5 AP: 180-212°F Curene 442: 235-250°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 104 - 113 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ASA S 310 | ROMIRA GmbH | ASA | Rotec® ASA |
| Generic Biodeg Polymers | Generic | Biodeg Polymers | Generic |
| GLAMIDE® T-661 | TOYOBO America, Inc. | Nylon 66 | GLAMIDE® |
| ICORENE® 4140 | ICO Polymers SA, A Division of A. Schulman | PE Copolymer | ICORENE® |
| LNP™ THERMOCOMP™ 5C003 compound | SABIC Innovative Plastics | PVDF | LNP™ THERMOCOMP™ |