Order Products : sales@su-jiao.com
Axiall PVC CL-7053
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | Axiall Corporation |
| Trademark: | Axiall PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iAcg3p_Axiall-PVC-CL-7053.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Georgia Gulf CL-7053 is a clear, high flow vinyl compound designed for a variety of end-use molding applications. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.40 | % | ASTM D955 |
| Flow Ratio 1(199 to 204°C) | 200 | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2620 | MPa | ASTM D638 |
| Tensile Strength | 45.5 | MPa | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C, 3.18 mm | 80 | J/m | |
| 23°C, 3.18 mm | 530 | J/m | |
| Gardner Impact (23°C) | 21.7 | J | ASTM D3029 |
| Drop Impact Resistance (23°C) | 138 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 70.0 | °C | |
| 1.8 MPa, Unannealed | 68.0 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | 34 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Shot Size | 35 to 75 | % | |
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 163 | °C | |
| Middle Temperature | 174 to 191 | °C | |
| Front Temperature | 182 to 193 | °C | |
| Nozzle Temperature | 177 to 193 | °C | |
| Processing (Melt) Temp | 202 to 210 | °C | |
| Mold Temperature | 15.6 to 48.9 | °C | |
| Injection Pressure | 82.7 to 138 | MPa | |
| Holding Pressure | 48.3 to 82.7 | MPa | |
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 25 to 80 | rpm | |
| Clamp Tonnage | 3.4 | kN/cm² | |
| Screw L/D Ratio | 16.0:1.0 to 24.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 to 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | Distance/Wall Thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH RZ310G6 | Polyram Ram-On Industries | PC | RAMTOUGH |
| Tecopet® PT74 CR30 BK111 PR | Eurotec Engineering Plastics | PET | Tecopet® |
| K-PU 7760 | Technovinyl Polymers India Ltd. | TPU, Unspecified | K-PU |
| ISPLEN® PM 750 AS | REPSOL | PP Homopolymer | ISPLEN® |
| LOXIM 800 00 HB | LOXIM Industries Private Limited | PP, Unspecified | LOXIM |