LNP™ LUBRICOMP™ XFL21R compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i9ywdi_LNP-LUBRICOMP-XFL21R-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP XFL21R is a compound based on Amorphous Nylon resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Mold Release. Also known as: LNP* LUBRICOMP* Compound XFL-4021 MR Product reorder name: XFL21R |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3740 | MPa | ASTM D638 |
| Tensile Strength (Break) | 84.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.1 | % | ASTM D638 |
| Flexural Modulus | 3900 | MPa | ASTM D790 |
| Flexural Strength | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 510 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 138 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 6.0 to 12 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 290 to 300 | °C | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 50.0 to 100 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCCPMI40 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| Sanren F850EBA (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| APEX® 3210-50NT | Teknor Apex Company | PVC, Flexible | APEX® |
| KMI KM TEC 132 | KMI Group, Inc. | Acrylic (SMMA) | KMI |
| Durethan® B 40 F 000000 | LANXESS Corporation | Nylon 6 | Durethan® |