Infino TK-2046HD
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i9RmHV_InfinoTK2046HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino TK-2046HD is a polycyclohexyldimethyl terephthalate (PCT) product, which contains a glass fiber reinforced material. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: mirrors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.53 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 60 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 66.0 | MPa | ASTM D638 |
| Yield | 58.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 2 | 2.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 3 | |||
| -- | 5500 | MPa | ASTM D790 |
| -- | 5400 | MPa | ISO 178 |
| Flexural Strength 4 | |||
| -- | 94.0 | MPa | ASTM D790 |
| -- | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 6(23°C) | 25 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 29 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 29 | J/m | ASTM D256 |
| 23°C 7 | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C, 3.18 mm | 300 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 290 | J/m | ASTM D256 |
| -5°C 8 | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 6.40mm | 245 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 245 | °C | ISO 75-2/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | ASTM D1925 | ||
| -- | 3.0 | YI | ASTM D1925 |
| 3.20 mm | 3.0 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Thickness: 4mm |
| 6 . | Thickness: 4mm |
| 7 . | Thickness: 4mm |
| 8 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silamid® EL | Roonamid a.s. | Nylon 6 | Silamid® |
| GELAST GT5HF | Guang Sung Plastics (GSPL) | SEBS | GELAST |
| Hostacom HBS831DC | LyondellBasell Industries | PP Copolymer | Hostacom |
| LG PMMA IH830 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| ESTOPLAST EP 2030GY50 | Ester Industries Ltd. | PBT | ESTOPLAST EP |