Shanghai Ofluorine PVDF M-1
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Shanghai Ofluorine Chemical Technology Co., Ltd |
| Trademark: | Shanghai Ofluorine PVDF |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i9GvbU_Shanghai-Ofluorine-PVDF-M-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PVDF homopolymer, with high melt viscosity, more suitable for compression molding. M-1 PVDF as raw materials, the finished products has excellent mechanical strength and tenacity. It can not be eroded by acid, alkali, strong oxidant, halogens. Good durability to aliphatic hydrocarbons, aromatic hydrocarbons, alcohol, aldehyde etc. In the work of hydrochloric acid, nitric acid, sulfuric acid, dilute alkali liquor, dense alkali liquor(40%) and 100°C temperature, its performance keep stable. Others, M-1 PVDF finished products has the properties of gamma-Ray resistant, UV resistant, and stability in wide temperature range. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/12.5 kg) | 1.0 to 4.0 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | < 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 to 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C | > 35.0 | MPa | |
| Break, 23°C | > 35.5 | MPa | |
| Tensile Elongation 2(Break, 23°C) | > 25 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature 3 | 165 to 171 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO S1005 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Multi-Flex® TPE A4710 SUV | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Clearflex® H&T CHH G0 | Versalis S.p.A. | VLDPE | Clearflex® H&T |
| Hifax TRC 103P R299 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| KEBAFLEX® U A 85 ST B01 natural | BARLOG plastics GmbH | TPU, Unspecified | KEBAFLEX® |