Order Products : sales@su-jiao.com
Clearflex® FG 368
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i8n7Gf_Clearflex-FG-368.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FG 368 is an octene comonomer linear low density polyethylene (C8-LLDPE), additivated with antioxidant and processing aid, suitable for blown film extrusion. Film manufactured with Clearflex FG 368 are characterised by high optical properties and outstanding mechanical properties. Main Application Clearflex FG 368 is recommended for the production of bioriented film in which a perfect combination between high mechanical properties, optical and sealing characteristics is required. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 230 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 250 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 12.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 45.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 550 | % | |
| TD : Break, 25 µm, Blown Film | 750 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 170 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 100.0 | kN/m | |
| TD : 25.0 µm | 250.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 107 | °C | ISO 306/A |
| Melting Temperature | 125 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 8.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PRC25UF0C-Black | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| AZDEL™ PM10400-701 | Azdel, Inc. | PP, Unspecified | AZDEL™ |
| Arnitel® PL381-H | DSM Engineering Plastics | TPC-ET | Arnitel® |
| DynaPath™ C4030CF | Polymer Dynamix | LCP | DynaPath™ |
| TECACOMP® PP ID blue 3956 | Ensinger GmbH | PP, Unspecified | TECACOMP® |