Niblan VCF10
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niblan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i7pQwr_Niblan-VCF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT reinforced with 10% short glass fibre. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.80 - 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3 | 3000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -22°C, 3.20 mm | 35 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | °C | ASTM D3418 |
| CLTE - Flow (23 to 55°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.0 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Surface Resistivity, IEC 60093: >1E15 ohmsVolume Resisitivity, IEC 60093: >1E15 ohm-cm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ G30H283 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| PRL PC-FR1-D | Polymer Resources Ltd. | PC | PRL |
| LUVOCOM® 1105-7794/BL VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Lupoy® GN1002FH | LG Chem Ltd. | PC | Lupoy® |
| LUVOCOM® 1105-8099/GY | LEHVOSS Group | PEEK | LUVOCOM® |