Tenogel® ABS A3 HL PRTA011 AB316
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Tenogel® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i7LOF4_Tenogel-ABS-A3-HL-PRTA011-AB316.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS resin for injection in black color, general purpose, excellent mechanical and thermal properties. Good resistance to impact, combined with high brightness and excellent low temperature performance, and good chemical resistance and easy processing. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 to 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 to 25 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (3.20 mm) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus 1 | 2200 | MPa | ASTM D790 |
| Flexural Strength 2 | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 195 to 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 3.0 mm/min |
| 2 . | 3.0 mm/min |
| 3 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravalene CR C 7644 | Ravago Group | LLDPE | Ravalene |
| Techsil IS808 | Techsil Limited | Silicone | Techsil |
| Softell CA 02 A | LyondellBasell Industries | Polyolefin, Unspecified | Softell |
| Xuchuan XCS-4575 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| LUVOCOM® 80-7050 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |