LNP™ VERTON™ MV00AS compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i6UfBy_LNPVERTONMV00AScompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled, heat stabilized Also known as: LNP* VERTON* Compound MFX-700-10 HS Product reorder name: MV00AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 11700 | MPa | ISO 178 |
| Flexural Stress | 209 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.34 | ASTM D3702 Modified | |
| With Self-Static | 0.52 | ASTM D3702 Modified | |
| Wear Factor - Washer | 73.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 27 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 159 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 - 243 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 249 - 260 | °C | |
| Processing (Melt) Temp | 221 - 249 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders T NAT BHV RX 2 | Arkema | Nylon 11 | Rilsan® Fine Powders |
| Safron® R101-01NU | Safripol (PTY) LTD | PP Random Copolymer | Safron® |
| EPO-TEK® OD2002 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| ISPLEN® PB 180 A4M | REPSOL | PP Impact Copolymer | ISPLEN® |
| Kazan LDPE 15813-020 OKP 22 1111 3202 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |