| PC/ABS-blend Flame retarded |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 57.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 7.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2600 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 101 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 106 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 132 | °C | ISO 306/A50 |
| -- | 118 | °C | ISO 306/B50 |
| Ball Pressure Test (110°C) | Pass | IEC 60695-10-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 2.50 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (1.60 mm) | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene HDPE ESD 201 B | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| APEX® 4109 | Teknor Apex Company | PVC, Flexible | APEX® |
| DENITER C 3010 | Vamp Tech | PC+PBT | DENITER |
| LNP™ LUBRICOMP™ 9X06483 compound | SABIC Innovative Plastics | Nylon 46 | LNP™ LUBRICOMP™ |
| Plasmer 2065N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |