EnCom PC-PBT 1013
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | EnCom, Inc. |
| Trademark: | EnCom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i5mu6d_EnCom-PC-PBT-1013.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Molding Grade PC/PBT Alloy |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 to 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 51.7 | MPa | ASTM D638 |
| Flexural Modulus | 2030 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 670 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 98.9 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 121 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 243 to 271 | °C | |
| Middle Temperature | 249 to 277 | °C | |
| Front Temperature | 257 to 282 | °C | |
| Nozzle Temperature | 254 to 274 | °C | |
| Processing (Melt) Temp | 260 to 279 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 75 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VDM93-30E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Gallonprene® GP520-6501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HAIPLEN H30 G5 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| LubriOne™ PC-000/20T | PolyOne Corporation | PC | LubriOne™ |
| MAJORIS HPS X790 | AD majoris | PPS | MAJORIS |