| PTFE Filled, Lubricated Polycarbonate Compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage (3.00 mm) | 0.50 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 3 | 2300 | MPa | ASTM D790 |
| Flexural Strength 4 | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 250 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 59 GB 10 | Plastcom | PP, Unspecified | SLOVALEN® |
| Multiuse Leostomer® LE-3140N | Riken Technos Corp. | TPU, Unspecified | Multiuse Leostomer® |
| NYCOA Polyamide 5300 HS | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| APEX® 90-A471R-75-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| apilon 52® D1 62L | API SpA | TPU-Polyester | apilon 52® |