Order Products : sales@su-jiao.com
PolyFibra® PF-PHF02
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | FuturaMat |
| Trademark: | PolyFibra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i4ox7n_PolyFibra-PF-PHF02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PF-PHF02 is a polypropylène and wood fibers (beech)-based product, an agromaterial descending from the PolyFibra® range. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 to 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.3 to 16 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 62 to 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1590 to 2190 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 22.0 to 36.0 | MPa | |
| Break | 20.0 to 34.0 | MPa | |
| Tensile Strain (Yield) | 3.5 to 5.7 | % | ISO 527-2 |
| Flexural Modulus | 1490 to 2330 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 15 to 27 | kJ/m² | ISO 179 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOYOBO PPS TS201 HS | TOYOBO America, Inc. | PPS | TOYOBO PPS |
| TPSiV™ 4000-50A | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| EPOXIDUR® EP 3581 T-1 | RASCHIG GmbH | Epoxy | EPOXIDUR® |
| LNP™ KONDUIT™ PX13322 compound | SABIC Innovative Plastics Asia Pacific | Nylon 6 | LNP™ KONDUIT™ |
| LUVOCOM® 1105-7336/GY7016 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |