Order Products : sales@su-jiao.com
PolyFibra® PF-PHF04
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | FuturaMat |
| Trademark: | PolyFibra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i4Zx1E_PolyFibra-PF-PHF04.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PF-PHF04 is an agromaterial descending from the PolyFibra range. PF-PHF04 is a Polypropylène and wood fibers (beech)-based product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 to 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.7 to 14 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 64 to 76 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1980 to 2740 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 22.0 to 36.0 | MPa | |
| Break | 21.0 to 35.0 | MPa | |
| Tensile Strain (Yield) | 2.3 to 3.9 | % | ISO 527-2 |
| Flexural Modulus | 2040 to 3180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 13 to 23 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 72.0 to 80.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2305 A FR | RTP Company | PUR, Unspecified | RTP |
| Toyolac® 450Y MH5 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Xuchuan XCY-5585EN | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Xuchuan XCW-6300T | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| TECHNYL® A 20 V35 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |