ASTAMID™ MB3GM24HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i4XRRG_ASTAMID-MB3GM24HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAMID™ MB3GM24HS is a highly heat stabilised combination 30% glass fibre and mineral filled Polyamide 6 grade. The product reinforcement levels are 10% glass fibres and 20% mineral. ASTAMID™ MB3GM24 HS has been developed for the automotive sector and is intended for metal replacement applications within the powertrain area. DRY indicates "Dry-As-Moulded" and WET indicates "Conditioned at 23 °C & 50% RH" |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.37 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | -- | % | ASTM D955 |
| Water Absorption | ||||
| 24 hr | 7.2 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (3.20 mm) | 6250 | 3650 | MPa | ASTM D638 |
| Tensile Strength (3.20 mm) | 105 | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm) | 4.0 | 12 | % | ASTM D638 |
| Flexural Modulus (3.20 mm) | 5500 | 2850 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm) | 162 | 82.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 1 | 5.0 | 9.0 | kJ/m² | ISO 179 |
| Notched Izod Impact 2(3.20 mm) | 55 | 95 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load 3 | ASTM D648 | |||
| 0.45 MPa, unannealed, 3.20mm | 215 | -- | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 175 | -- | °C | ASTM D648 |
| CLTE - Flow | 4.2E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 260 - 270 | °C | |
| Front Temperature | 270 - 280 | °C | |
| Processing (Melt) Temp | 275 - 290 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Pressure | 60.0 - 140 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 5.0 - 9.0 | kN/cm² |
| Injection instructions |
|---|
| Drying Time (Opened Bag): >12 hrDrying Time (Unopened Bag): 2 hr |
| Note Message | |
|---|---|
| 1 . | 10 x 4 mm |
| 2 . | 12.7 x 3.2 mm |
| 3 . | 12.7 x 3.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN 6060 | Saudi Polymers Company | HDPE | Marlex® |
| THERMOLAST® K TF6WKF (Series: DW) | KRAIBURG TPE | TPE | THERMOLAST® K |
| NYCOA NanoTUFF™ NT-90-100 | Nycoa (Nylon Corporation of America) | Nylon 612 | NYCOA NanoTUFF™ |
| Gallonprene® GP520-6502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Delon 5050 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | Delon |