XENOY™ 5220U resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i4FkZg_XENOY5220Uresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 | g/cm³ | ASTM D792 |
| -- | 1.22 | g/cm³ | ISO 1183 |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 16 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 15.0 | cm³/10min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.80 - 1.0 | % | Internal method |
| Transverse flow 1 | 0.80 - 1.0 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Outdoor Suitability | f2 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2250 | MPa | ASTM D638 |
| -- 3 | 2250 | MPa | ASTM D638 |
| -- | 2050 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 53.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Fracture 5 | 51.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 6 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture 7 | 120 | % | ASTM D638 |
| Fracture | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 8 | 2030 | MPa | ASTM D790 |
| -- 9 | 2000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0mm span 10 | 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11(23°C) | 55 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -40°C | 300 | J/m | ASTM D256 |
| -30°C | 530 | J/m | ASTM D256 |
| 23°C | 710 | J/m | ASTM D256 |
| -30°C 12 | 30 | kJ/m² | ISO 180/1A |
| 23°C 13 | 50 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 107 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 84.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 99.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 75.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 122 | °C | ASTM D1525 15 |
| -- | 120 | °C | ISO 306/B50 |
| -- | 125 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 9.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| RTI Elec | 75.0 | °C | UL 746 |
| RTI Imp | 75.0 | °C | UL 746 |
| RTI | 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 16 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 - 80 | % | |
| Rear Temperature | 243 - 266 | °C | |
| Middle Temperature | 249 - 271 | °C | |
| Front Temperature | 254 - 277 | °C | |
| Nozzle Temperature | 254 - 271 | °C | |
| Processing (Melt) Temp | 260 - 277 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 116 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 1.0E-3 - 0.020 | % | |
| Cylinder Zone 1 Temp. | 171 - 204 | °C | |
| Cylinder Zone 2 Temp. | 193 - 254 | °C | |
| Cylinder Zone 3 Temp. | 204 - 282 | °C | |
| Cylinder Zone 4 Temp. | 204 - 282 | °C | |
| Adapter Temperature | 227 - 282 | °C | |
| Melt Temperature | 243 - 277 | °C | |
| Die Temperature | 232 - 282 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrsRoll Stack Temp - Bottom: 82 - 93 °CRoll Stack Temp - Middle: 77 - 82 °CRoll Stack Temp - Top: 71 - 82 °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | 50 mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | Type 1, 50mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| 16 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANTEC PC S75R GF10 V0 | Polykemi AB | PC | SCANTEC |
| STRANOX PA6/ST/45%LFT | Oxford Polymers | Nylon 6 | STRANOX |
| Next Nylon 66 Prime Series PG25-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| ALCOM® POM 770/1 PTFE20 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALCOM® POM |
| Aplax P2812GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |