DOW™ LDPE 132I
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i2yazF_DOW-LDPE-132I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 5.71 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 216 | J/cm³ | ASTM D882 |
| TD : 51 µm | 211 | J/cm³ | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 12.1 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.1 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 31.8 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 28.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 470 | % | ASTM D882 |
| TD : Fracture, 51 µm | 660 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 190 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 300 | g | ASTM D1922 |
| TD : 51 µm | 180 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.1 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 110 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 50 | ASTM D2457 | |
| Haze (50.8 µm) | 11 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；30:1 L/D 螺杆类型：单跨双混合 模具间隙：40 密尔 (1.02 mm) 熔体温度：420°F (215°C) 输出：模具周长的 8 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M30CHPP10 | McCann Plastics Inc. | PP Homopolymer | McCann PP |
| RTP 1000 TFE 20 | RTP Company | PBT | RTP |
| SEETEC EVA VS410 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| ALCUDIA® HDPE 5300-N | REPSOL | HDPE, HMW | ALCUDIA® HDPE |
| DOMAMID® 6G50AFHUV | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |