ARNYL PA66 30% FV INDUSTRIALE NERO
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Daloga srl |
| Trademark: | ARNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i2Z5WW_ARNYL-PA66-30-FV-INDUSTRIALE-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ARNYL PA66 30% FV INDUSTRIALE NERO is a Polyamide 66 (Nylon 66) material. It is available in Europe. Typical application of ARNYL PA66 30% FV INDUSTRIALE NERO: Industrial Applications |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Ash Content - 1 hrs (750°C) | 28 to 32 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ASTM D638 |
| Tensile Strength (Break) | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus | 7500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 260 | °C | |
| 1.8 MPa, Unannealed | 255 | °C | |
| Vicat Softening Temperature | |||
| -- | 260 | °C | ASTM D1525 1 |
| -- | 255 | °C | ASTM D1525 2 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNOGRAN® PCI BLK | Eurocompound Polymers | PC | TECHNOGRAN® |
| TRIMID® N66-G13L | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| Beetafin® ULS9010 | BIP (Oldbury) Limited | PUR-Ester | Beetafin® |
| Geon™ Vinyl Packaging UV-SORB-1 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Packaging |
| ICORENE® N9205 | ICO Polymers EMEA, A Division of A. Schulman | PET | ICORENE® |