Ateva® 1813
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i2Pngv_Ateva-1813.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for high quality microcellular crosslinked foam applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.937 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.6 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 93 | ||
| Shore D | 37 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 740 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 48.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 64.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 88.0 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP JOSB26624 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| ADMER™ NE062E | Mitsui Chemicals Europe GmbH | PE, Unspecified | ADMER™ |
| Arak HDPE BL4 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| E-RIALGLASS H 15 S 30 TG | RIALTI Srl | PP Homopolymer | E-RIALGLASS |
| HiFill® PFA 4450 | Techmer Engineered Solutions | PFA | HiFill® |