Tecopet® PT74 CR30 BK111 PR
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecopet® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i1YRTc_Tecopet-PT74-CR30-BK111-PR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PET, 30% carbon fiber reinforced, black, fast crystallization grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 0.080 | % | ISO 15512 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 24000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 180 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 | hr | |
| Hopper Temperature | 50.0 to 70.0 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 60.0 to 100 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 14CNF30-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Flontech® FT-CAF20-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| DuraFlex 416 | Evermore Chemical Industry Co., Ltd. | TPU-Polyether | DuraFlex |
| Hapflex™ 660-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Karina IVORY PVC COMPOUND CAK 35-F | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |