VESTODUR® X9405

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	Evonik Industries AG
Trademark:	VESTODUR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	i1N8GC_VESTODUR-X9405.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Evonik manufactures a range of polybutylene terephthalate compounds that are supplied under the registered trademark VESTODUR®. Material properties characterizing VESTODUR® compounds are:

high thermostability

high stiffness

low water absorption resulting in high dimensional stability

high hardness

good strength

good sliding friction behavior, low abrasion

good creep behavior

good electrical properties

good chemical resistance

good weathering resistance

good processability

no tendency to form stress cracks

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Features	Good Abrasion Resistance Good Chemical Resistance Good Creep Resistance Good Dimensional Stability Good Electrical Properties Good Processability Good Strength Good Thermal Stability Good Weather Resistance High Hardness High Stiffness Low to No Water Absorption
Uses	Automotive Applications Fuel Lines Thin-walled Parts Wire & Cable Applications
Appearance	Colors Available Natural Color
Forms	Granules
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.70	g/cm³	ISO 1183
Molding Shrinkage			ISO 294-4
Across Flow	1.7	%
Flow	0.20	%
Water Absorption (Saturation, 23°C)	0.70	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	80		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	9000	MPa	ISO 527-2
Tensile Stress	90.0	MPa	ISO 527-2/50
Tensile Strain (Break)	3.2	%	ISO 527-2/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C, Complete Break	13	kJ/m²
23°C, Complete Break	18	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C, Complete Break	80	kJ/m²
23°C, Complete Break	80	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	223	°C	ISO 75-2/B
1.8 MPa, Unannealed	210	°C	ISO 75-2/A
Vicat Softening Temperature
--	222	°C	ISO 306/A
--	210	°C	ISO 306/B
Melting Temperature	221 to 226	°C	ISO 11357-3
CLTE			ISO 11359-2
Flow : 23 to 55°C	3.0E-5	cm/cm/°C
Transverse : 23 to 55°C	6.0E-5	cm/cm/°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+13	ohms	IEC 60093
Volume Resistivity (23°C)	1.0E+15	ohms·cm	IEC 60093
Electric Strength ¹(1.00 mm, in Oil)	27	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	4.10
23°C, 1 MHz	3.70
Dissipation Factor			IEC 60250
23°C, 100 Hz	8.0E-3
23°C, 1 MHz	0.022
Comparative Tracking Index			IEC 60112
-- ²	325	V
Solution A	350	V

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.400 mm	V-0
0.800 mm	V-0
1.60 mm	V-0
Glow Wire Flammability Index (2.00 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (2.00 mm)	775	°C	IEC 60695-2-13

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion	A1 step		IEC 60426

Note Message
1 .	K 20/P 50
2 .	100 Drops value

Resin Grade	Manufacturer	Category	Trademark
Santron IMS2007LF	Bhansali Engineering Polymers Limited	SAN	Santron
Braskem PP C711-70RNA	Braskem Europe GmbH	PP Impact Copolymer	Braskem PP
Elastollan® 1160 A 13 P 000	BASF Polyurethanes GmbH	TPU-Polyether	Elastollan®
Lifoflex® UV 30 GC 1030	ELASTO	SEBS	Lifoflex®
Durethan® AC 30 DUS027 000000	LANXESS Asia/Pacific	Nylon 66	Durethan®