Hapflex™ 766
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Hapflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i0B3AM_Hapflex-766.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HAPFLEX 700 & 800 products are a series of low hazard, colorless, high strength, elastomers available in Shore hardnesses from 65A to 72D. HAPFLEX 700 & 800 products exhibit high tensile strength, high tear strength, and excellent elongation. All HAPFLEX 700 & 800 products cure at room temperature and can be accelerated with heat. Another key attribute of the 700 & 800 SERIES is that the base color of all components is colorless. For user convenience, HAPCO has designed this series in 2 speeds so the user can "customize" production rates and cure times. The fast and regular versions can be blended to user customize the gel time and cure time. HAPFLEX 700 & 800 SERIES can be used for mechanical, electrical, and mechanical/electrical applications. In addition, HAPFLEX 700 & 800 products show superior water immersion properties and superior adhesion when used in combination with Hapco's one part PRIMER 200. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 17 | g |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 23.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 5.52 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 950 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 29.8 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 | |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 20, Mix Ratio by Volume: 20 | ||
| Thermoset Mix Viscosity (25°C) | 4000 | cP | ASTM D4878 |
| Demold Time (21°C) | 960 to 1400 | min | Internal Method |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYREX® PH-88S | CHI MEI CORPORATION | PS (HIPS) | POLYREX® |
| Shin-Etsu RTV KE-441 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| AURATHENE HDUFBK | Aurora Manufacturing Ltd | HDPE | AURATHENE |
| KEBAFORM® C 901 CB | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Paryls® PPSU F1150 | Youju New Materials Co., Ltd. | PPSU | Paryls® |