LUVOCOM® 3-7234-1 Datasheet,Nylon 6,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®3-7234-1 is a polyamide 6 (nylon 6) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 3-7234-1 are: flame retardant/rated flame Conductivity Antistatic Good stiffness Wear-resistant Typical application areas include: engineering/industrial accessories House textile/fiber Automotive Industry Handle

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Additive	Antistatic property
Features	Conductivity Rigid, good Antistatic property Good strength Good wear resistance
Uses	Handle Textile applications Engineering accessories Roller Application in Automobile Field Shell
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.21	g/cm³	ISO 1183
Molding Shrinkage	0.40 - 0.80	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.3	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	9000	MPa	ISO 527-2
Tensile Stress (Break)	130	MPa	ISO 527-2
Tensile Strain (Yield)	3.0	%	ISO 527-2
Flexural Modulus	7000	MPa	ISO 178
Flexural Stress	190	MPa	ISO 178
Coefficient of Friction
Dynamic	0.24
Static	0.21
Flexural Strain at Flexural Strength	4.0	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	130	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	1.0E+3	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	45	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	200	°C	ISO 75-2/A
Continuous Use Temperature	90.0	°C	UL 746B
Vicat Softening Temperature	220	°C	ISO 306/A
CLTE - Flow	2.5E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.30	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+3 - 1.0E+5	ohms	IEC 60093

Flammability	Nominal Value	Unit	Test Method
Flame Rating	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature
A	75.0	°C
B	105	°C
Drying Time
A	10 - 16	hr
B	4.0 - 6.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	250 - 270	°C
Middle Temperature	270 - 290	°C
Front Temperature	280 - 300	°C
Nozzle Temperature	270 - 280	°C
Processing (Melt) Temp	270	°C
Mold Temperature	70.0 - 110	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	hzczg5_LUVOCOM-3-7234-1.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 2181 TFE 15 SI 2	RTP Company	PEI	RTP
RTP 800 SI 2 Z	RTP Company	Acetal (POM) Copolymer	RTP
Wellamid® GF1927-N1	Wellman Engineering Resins	Nylon 66	Wellamid®
Complet® LCF40-PP	PlastiComp, Inc.	PP Homopolymer	Complet®
LNP™ LUBRICOMP™ Lexan_LF0335 compound	SABIC Innovative Plastics Europe	PC	LNP™ LUBRICOMP™