Shinko-Lac® ABS VM-1
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hyinwc_Shinko-Lac-ABS-VM-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS VM-1 is a flame retardant grade that offers excellent flame retardant characteristics to products along with good thermal stability. Good flow property offers easy processing especially for large and thin products. VM-1 also exhibits excellent plating characteristics. Typical applications of VM-1 include electrical/electronic applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2450 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 40.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 64.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 80.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm, NC | V-2 | UL 94 | |
| 3.18 mm, NC | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 200 - 250 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 200 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ L90 | Miracll Chemicals Co., Ltd. | TPU-Capro | Mirathane™ |
| Starflex GM1510BA | LyondellBasell Industries | mLLDPE | Starflex |
| TOTAL Polyethylene XSene® HDPE XRC20 Orange | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| HANWHA 3392 | Hanwha Chemical | HDPE | HANWHA |
| IDI SMC S30 (Glass Content 30%) | IDI Composites International | TS, Unspecified | IDI SMC |