Vydyne® 47H BK0668
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hyBG0e_Vydyne-47H-BK0668.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 47H BK0668 is a high-performance, medium-impact-modified, heat-stabilized grade of PA66 resin. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 1.6 | -- | % | |
| Flow : 23°C, 2.00 mm | 1.8 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2780 | 1740 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 60.0 | 45.0 | MPa | |
| Break, 23°C | 52.0 | 40.0 | MPa | |
| Tensile Strain (Break, 23°C) | 22 | 60 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2300 | 780 | MPa | ISO 178 |
| Flexural Strength (23°C) | 70.0 | 24.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 11 | 18 | kJ/m² | |
| -30°C | 17 | 24 | kJ/m² | |
| 23°C | 19 | 62 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 12 | 18 | kJ/m² | |
| -30°C | 16 | 24 | kJ/m² | |
| 23°C | 18 | 44 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 185 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 63.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.4E-4 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 115 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 115 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (0.750 mm) | 1.0E+11 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 12 | -- | kV/mm | IEC 60243 |
| Arc Resistance | PLC 6 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 525 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.750 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 4 | -- | ||
| 3.00 mm | PLC 3 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 700 | -- | °C | |
| 1.50 mm | 775 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 725 | -- | °C | |
| 1.50 mm | 800 | -- | °C | |
| 3.00 mm | 725 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Automotive Materials - (thickness d = 1 mm) | + | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ NM-818.H001-8046 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| ESENTTIA 03H83 | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Ingeo™ 6252D | NatureWorks® LLC | PLA | Ingeo™ |
| Lionpol IM-31050 | Lion Polymers Incorporated | TPE | Lionpol |
| KOPPS® S15G30HIBL | Kolon Plastics, Inc. | PPS | KOPPS® |