SUMIKASUPER® LCP E5008
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKASUPER® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hxrUDW_SUMIKASUPER-LCP-E5008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.69 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.060 | % | |
| Across Flow | 1.3 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 111 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.8 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 12200 | MPa | |
| 200°C | 5880 | MPa | |
| Flexural Strength | ASTM D790 | ||
| 23°C | 127 | MPa | |
| 200°C | 39.0 | MPa | |
| Shear Strength | 50.0 | MPa | ASTM D732 |
| Poisson's Ratio | 0.41 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.40 mm) | 88 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.40 mm) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 335 | °C | ASTM D648 |
| CLTE | Internal Method | ||
| Flow : 150°C | 1.0E-6 | cm/cm/°C | |
| Transverse : 150°C | 6.4E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.56 | W/m/K | JIS R2618 |
| RTI Elec (3.20 mm) | 240 | °C | UL 746 |
| RTI Imp (3.20 mm) | 220 | °C | UL 746 |
| RTI Str (3.20 mm) | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | > 40 | kV/mm | Internal Method |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.70 | ||
| 1 MHz | 4.20 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.015 | ||
| 1 MHz | 0.031 | ||
| Arc Resistance | 128 | sec | ASTM D495 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.300 mm, ALL) | V-0 | UL 94 | |
| Oxygen Index | 47 | % | JIS K7201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soldering Resistance | 340 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 4.0 to 24 | hr | |
| Rear Temperature | 350 to 370 | °C | |
| Middle Temperature | 370 to 390 | °C | |
| Front Temperature | 390 to 410 | °C | |
| Nozzle Temperature | 390 to 410 | °C | |
| Processing (Melt) Temp | 400 | °C | |
| Mold Temperature | 40.0 to 160 | °C | |
| Injection Pressure | 120 to 160 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 to 60.0 | MPa | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ELASTOSIL® N 288 | Wacker Chemie AG | Silicone | ELASTOSIL® N |
| Elastron® G G500.A80.N.ABS | Elastron USA, Inc. | SEBS | Elastron® G |
| ENGAGE™ 8452 EL | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| Lastil G/30 | LATI S.p.A. | SAN | Lastil |
| InnoPlus LL7420A | PTT Global Chemical Public Company Limited | LLDPE | InnoPlus |