DOWLEX™ 2629.10UE
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hxlKRB_DOWLEX-2629-10UE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2629UE Polyethylene Resin for rotational and injection moulding is specifically designed for applications requiring excellent environmental stress crack resistance and impact strength combined with low warpage and good processing. Processing and Stabilisation: DOWLEX™ 2629UE Polyethylene Resin is fully heat and UV stabilised resulting in a wide processing latitude, good colour retention and long life expectancy. The powder version is named DOWLEX™ 2629.10UE Polyethylene Resin. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.935 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 10% Antarox, Compression Molded | 400 | hr | |
| 50°C, 100% Antarox, Compression Molded | > 1000 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 57 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, Compression Molded) | 17.5 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | 650 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 645 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Multi-Axial Instrumented Impact Energy 1 | ISO 6603-2 | ||
| -20°C, Rotational Molded | 66.0 to 88.0 | J | |
| 23°C, Rotational Molded | 54.0 to 72.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 65.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 119 | °C | ASTM D1525 2 |
| Melting Temperature | 124 | °C | DSC |
| Peak Crystallization Temperature (DSC) | 110 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | Plates of 3-4 mm thickness. |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III HDPE6205B | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| TEKNIFLEX® Pouch CS6023 | Tekni-Films, a div of Tekni-Plex | Film, C1S Paper/LDPE/Al Foil/Surlyn | TEKNIFLEX® Pouch |
| Vydyne® 49 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Dural 202/3 CLEAR 0003 | AlphaGary | PVC, Rigid | Dural |
| Jamplast EX-01 | Jamplast, Inc. | PVC, Unspecified | Jamplast |