HiFill® PA6 CF40
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hwsIgB_HiFill-PA6-CF40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PA6 CF40 is a Polyamide 6 (Nylon 6) product filled with 40% carbon fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 221 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 20700 | MPa | ASTM D790 |
| Flexural Strength | 324 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 210 | °C | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 260 to 304 | °C | |
| Processing (Melt) Temp | 243 to 271 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2107 Z | RTP Company | PEI | RTP |
| MERICAN® -9406 | Huachang Polymer Co., Ltd. | Polyester Alloy | MERICAN® |
| NEXT REPROCESSED PPC SB891-300R | NEXT Specialty Resins, Inc. | PP Impact Copolymer | NEXT REPROCESSED |
| Kpren CM435 | Shandong Xuye New Materials Co., Ltd. | CM | Kpren |
| OTECH TPO OTO7510EP1 - Automotive | OTECH Corporation | TPO | OTECH TPO |