CERTENE™ LDF-222A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hwIKID_CERTENE-LDF-222A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LDF-222A is a certified prime resin specially designed for production of high clarity Blown films for packaging of articles requiring good opticals such as baked products, sandwich bags, light duty produce bags, toilette paper and textiles. LDF-222A features easy processability, and optimal balance of film strength, stiffness, good openability and excellent sealability. Maximum recommended film drawdown is 1.0 mil. LDF-222A contains no slip and no antiblock. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm | 234 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm | 248 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm | 11.0 | MPa | ASTM D882 |
| MD : Broken, 32 µm | 26.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm | 15.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm | 180 | % | ASTM D882 |
| TD : Broken, 32 µm | 550 | % | ASTM D882 |
| Dart Drop Impact (32 µm) | 85 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm | 540 | g | ASTM D1922 |
| TD : 32 µm | 160 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm) | 75 | ASTM D2457 | |
| Haze (31.8 µm) | 5.3 | % | ASTM D1003 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 175 - 185 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P490 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| MFE® -10 | Huachang Polymer Co., Ltd. | Vinyl Ester | MFE® |
| Hostaform® C 52021 XAP | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Laprene® 830000808 | SO.F.TER. SPA | SEBS | Laprene® |
| K-vinyl 105 Deg C Rating Insulation (85-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |