Michimid K4100GF33-02
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michimid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hv9iHA_Michimid-K4100GF33-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michimid K4100GF33-02 is a Polyamide 6 (Nylon 6) product filled with 33% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 155 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 8270 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 204 | °C | |
| Melting Temperature | 215 | °C | ASTM D789 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 271 | °C | |
| Front Temperature | 271 | °C | |
| Nozzle Temperature | 266 | °C | |
| Processing (Melt) Temp | 277 | °C | |
| Mold Temperature | 79.4 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melinex® 052 | DuPont Teijin Films U.S. | Polyester, TP | Melinex® |
| SMOKEGUARD™ O 204 NATURAL | AlphaGary | Polyolefin, Unspecified | SMOKEGUARD™ O |
| Petrothene® GA672962 | LyondellBasell Industries | HDPE | Petrothene® |
| KMI PA KM66-01NAT | KMI Group, Inc. | Nylon 66 | KMI PA |
| LNP™ LUBRICOMP™ RP003 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |