Braskem PE PLURIS4301
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | huwyce_Braskem-PE-PLURIS4301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pluris4301 is a Braskem Quaterpolymer produced with Spherilene technology. This grade show unique properties, such as high stiffness associated with toughness. In addition to good processability, also shows a very good bubble stability and very low gel content. Applications: Thin films and automatic packaging which require higher stiffness: textile products, toilet paper and others. Additive:
Process: Blown Film Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 32.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 33.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 920 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1500 | % | ASTM D882 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 38 µm | 310 | MPa | ASTM D790 |
| 1% Secant, TD : 38 µm | 400 | MPa | ASTM D790 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 50 | g | ASTM D1922 |
| TD : 38 µm | 300 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm) | 45 | ASTM D2457 | |
| Haze | 43 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Recommended Blown Film Extrusion Conditions: Temperature Profile: 150°C to 170°C Blow Up Ratio: 2 to 3:1 Die Gap: 1.8 to 2.5 mm Mass Temperature: 160° to 200°C It's Recommended to add 20 to 30% LDPE to be obtained excellent optical propert |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 150 HF | RTP Company | PP, Unspecified | RTP |
| Starflam RF0052E | Eurostar Engineering Plastics | Nylon 66/6 | Starflam |
| Wondel® P PG4 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| Pearlthane® 11T75D | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| Hifax TRC 432X BLACK | LyondellBasell Industries | PP Copolymer | Hifax |